AKROMID®
A3 GK 30 LA black (4624)
PA66 GB30
AKROMID® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.
5.000MPa
90MPa
25kJ/m²
AKROMID® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.
AKROLOY®
PA FGF 60 black (6765)
PA66 + PA6I/6T GF 60
AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction
20.000MPa
290MPa
90kJ/m²
AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction
AKROMID®
B3 GF 15 natural (2469)
PA6 GF15
AKROMID® B3 GF 15 natural (2469) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color
6.100MPa
120MPa
52kJ/m²
AKROMID® B3 GF 15 natural (2469) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color
AKROTEK®
PK-VM black (4973)
PK
AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance
1.500MPa
60MPa
180kJ/m²
AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance
AKROMID®
C3 GF 35 1 natural (4748)
PA66+PA6 GF35
AKROMID® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.000MPa
200MPa
100kJ/m²
AKROMID® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROTEK®
PK-VM CF 10 TM black (6135)
PK CF10
AKROTEK® PK-VM CF 10 TM black (6135) - Polyketon, 10% carbon fiber reinforced, chemical, tribological modification, high elongation at break
3.500MPa
59MPa
100kJ/m²
AKROTEK® PK-VM CF 10 TM black (6135) - Polyketon, 10% carbon fiber reinforced, chemical, tribological modification, high elongation at break
AKROMID®
B3 9 natural (6409)
PA6
AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland
3.300MPa
85MPa
NA
AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland
PRECITE®
P3 S1 black (7522)PBT I
PRECITE® P3 S1 black (7522) is an unreinforced, medium viscosity polybutylene terephthalate (PBT) with high impact strength. Due to its low moisture absorption, this material has very good dimensional stability. It is particularly suitable for precision parts in the automotive, E&E or appliances industry.
Features
Properties
1.750MPa
40MPa
180kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at yield
ISO 527-2
Tensile strain at yield
ISO 527-2
Tensile stress at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Vicat softening temperature B50
ISO 306
Flammability
Burning rate
UL 94
General properties
Density
ISO 1183
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.