Find the right compound
Select your fitting and find the right compound for your intend
AKROLOY®
PA FGF 60 black (6765)
PA66 + PA6I/6T GF 60
AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction
20.000MPa
290MPa
90kJ/m²
AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction
AKROMID®
B3 GF 50 ECO black (7926)
PA6 GF50
AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.
16.000MPa
200MPa
95kJ/m²
AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.
AKROMID®
T5 GF 50 natural (7834)
PPA GF50
AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
18.500MPa
275MPa
95kJ/m²
AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications
AKROLOY®
PARA ICF 40 black (6130)
PARA CF40
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
39.000MPa
280MPa
35kJ/m²
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
AKROMID®
B3 S1 natural (7748)
PA6-I
AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6
1.350MPa
35MPa
180kJ/m²
AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6
AKROMID®
C3 1 S3 black (4297)
PA66+PA6
AKROMID® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems
2.500MPa
65MPa
180kJ/m²
AKROMID® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems
AKROMID®
B3 GM 10/20 1 black (8748)
PA6 (GF10+GB20)
AKROMID® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
5.700MPa
110MPa
30kJ/m²
AKROMID® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
AKROLOY®
PA GF 50 8 black (6732)PA66+PA6I/6T GF50
AKROLOY® PA GF 50 8 black (6732) is a 50% glass fiber reinforced, semi-aromatic polyamide blend. It is characterised by lower moisture absorption compared to standard PA 6.6 compounds, thus convincing through very high stiffness and strength even in the conditioned state. The material is therefore perfectly suitable for technical applications with high demands for dimensional stability. Furthermore, it can be used as an alternative for aluminium and zinc diecast alloys. The compound fulfill FDA, EU10/2011 and ACS.
Features
Regulatory
Properties
17.500MPa
260MPa
105kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.