AKROMID®
C3 1 S3 black (4297)
PA66+PA6
AKROMID® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems
2.500MPa
65MPa
180kJ/m²
AKROMID® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems
AKROMID®
B3 GM 10/20 1 black (8748)
PA6 (GF10+GB20)
AKROMID® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
5.700MPa
110MPa
30kJ/m²
AKROMID® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
AKROTEK®
PK-VM black (4973)
PK
AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance
1.500MPa
60MPa
180kJ/m²
AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance
AKROMID®
A3 ICF 30 5 black (6495)
PA66 CF30
AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties
23.000MPa
235MPa
50kJ/m²
AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties
AKROLOY®
PARA ICF 40 black (6130)
PARA CF40
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
39.000MPa
280MPa
35kJ/m²
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
AKROMID®
B3 S1 natural (7748)
PA6-I
AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6
1.350MPa
35MPa
180kJ/m²
AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6
AKROMID®
A3 GF 30 1 L natural (4715)
PA66+PP GF30
AKROMID® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride
8.600MPa
155MPa
77kJ/m²
AKROMID® A3 GF 30 1 L natural (4715) - PA6.6/PP-Blend, 30% glass fibre reinforced, lower density, cost reduced, zinc chloride
AKROMID®
AKROMID® B3 GM 10/20 1 L black (4646) is a PA6/PP-blend with reduced density compared to standard PA6 GM 10/20. With 10% glass fibre reinforcement and 20% glass bead filling the material is suitable for components with average strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMID® B3 GM 10/20 1 L black (4646) is particularly superior to calcium chloride (CaCl₂).
Features
Properties
5.100MPa
88MPa
46kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.