AKROMID®

T5 GF 50 8 black (6205)

PPA GF50

AKROMID® T5 GF 50 8 black (6205) - PPA, 50% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

19.000MPa

Strength

270MPa

Impact

85kJ/m²

AKROMID® T5 GF 50 8 black (6205) - PPA, 50% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROLOY®

Preliminary

PA FGF 60 black (6765)

PA66 + PA6I/6T GF 60

AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction

Modulus

20.000MPa

Strength

290MPa

Impact

90kJ/m²

AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction

AKROMID®

B3 GF 40 5 black (7286)

PA6 GF40

AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 35 1 black (2486)

PA6 GF35

AKROMID® B3 GF 35 1 black (2486) is a 35% glass fibre reinforced, heat stabilised Polyamid 6 with high stiffness and strength.

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 1 black (2486) is a 35% glass fibre reinforced, heat stabilised Polyamid 6 with high stiffness and strength.

AKROMID®

B3 ICF 10 1 black (6194)

PA6 CF10

AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties

Modulus

8.500MPa

Strength

125MPa

Impact

45kJ/m²

AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties

AKROMID®

UL

B3 1 FR natural (6437)

PA6 FR(30)

AKROMID® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.500MPa

Strength

75MPa

Impact

85kJ/m²

AKROMID® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROMID®

UL

A3 GF 30 HU grey (6600)

PA66 GF30

AKROMID® A3 GF 30 HU grey (6600) is a 30% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength, listet at UL in all colors

Modulus

10.500MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 HU grey (6600) is a 30% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength, listet at UL in all colors

143444580

AKROMID®

Preliminary
Internal

NEXT 5.6 3 GF 35 9 FR natural (8401)PA56 GF35 FR(40)

AKROMID® NEXT 5.6 3 GF 35 9 FR natural (8401) is a partially bio-based and flame retardant PA 5.6 and meets the requirement according to UL94 V0 @ 1.6 mm. The flame-retardant system is free of red phosphorus and halogens. PA 5.6 is a HMD-free (hexamethylenediamine) alternative to PA 6.6. With 35% glass fibre reinforcement, the material is suitable for components with high strength requirements for E&E and E-Mobility, such as busbar supports, switches, terminal strips and connector housings.

Features

Bio-based
heat stabilised 130
flame retardant
E&E

Properties

Modulus

12.000MPa

Strength

160MPa

Impact

71kJ/m²

Sustainability

Biobased carbon content

35 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12500 MPa
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
255 MPa
160 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
4,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
71 kJ/m²
70 kJ/m²
69 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
15 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
254 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
900 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
725 °C
725 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,43 g/cm³

Water absorption

ISO 62

23°C, saturated
2,0 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.