AKROMID®

A3 GF 30 6 natural (6398)

PA66 GF30

AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength

Modulus

10.000MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength

AKROMID®

B28 GF 35 FR EN black (7484)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.

AKROMID®

Preliminary

T9 GF 30 grey (8134)

PPA GF30

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

Modulus

10.000MPa

Strength

190MPa

Impact

70kJ/m²

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

AKROMID®

B3 GF 50 1 grey (5507)

PA6 GF50

AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.500MPa

Strength

190MPa

Impact

70kJ/m²

AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 15 grey (6270)

PA6 GF15

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

Modulus

6.000MPa

Strength

110MPa

Impact

50kJ/m²

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

AKROMID®

UL

B3 1 FR orange (7698)

PA6 FR(30)

AKROMID® B3 1 FR orange (7698) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.600MPa

Strength

75MPa

Impact

NA

AKROMID® B3 1 FR orange (7698) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

PRECITE®

P3 GF 10 black (7813)

PBT GF 10

PRECITE® P3 GF 10 black (7813) is a 10% glass fibre reinforced, medium viscous poly(butylene terephthalate) with medium stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

4.600MPa

Strength

90MPa

Impact

25kJ/m²

PRECITE® P3 GF 10 black (7813) is a 10% glass fibre reinforced, medium viscous poly(butylene terephthalate) with medium stiffness and toughness as well as high dimensional and chemical resistance.

143444580

AKROMID®

B3 GF 30 RM-M natural (3291)PA6 + X GF30

AKROMID® B3 GF 30 RM-M natural (3291) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical changes in the conditioned state. It is therefore perfectly suitable for components where high dimensional stability is required, e.g. in sports and leisure. The material has a light inherent color.

Features

reduced moisture

Properties

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
7100 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
165 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,6 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
9600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
70 kJ/m²
70 kJ/m²
65 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
12 kJ/m²
15 kJ/m²
10 kJ/m²
10 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
160 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,41 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,65 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.