AKROMID®

B3 GFM 10/20 1 black (2017)

PA6 (GF10+M20)

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

Modulus

6.200MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

AKROMID®

A3 GF 20 1 black (2307)

PA66 GF20

AKROMID® A3 GF 20 1 black (2307) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength.

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID® A3 GF 20 1 black (2307) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength.

AKROMID®

A3 GF 35 1 natural (2393)

PA66 GF35

AKROMID® A3 GF 35 1 natural (2393) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.600MPa

Strength

215MPa

Impact

92kJ/m²

AKROMID® A3 GF 35 1 natural (2393) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 15 natural (2469)

PA6 GF15

AKROMID® B3 GF 15 natural (2469) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/m²

AKROMID® B3 GF 15 natural (2469) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color

AKROMID®

B3 GF 25 1 L black (4637)

PA6+PP GF25

AKROMID® B3 GF 25 1 L black (4637) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

7.500MPa

Strength

135MPa

Impact

68kJ/m²

AKROMID® B3 GF 25 1 L black (4637) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMID®

A3 GM 25/15 1 black (7003)

PA66 (GF25+GB15)

AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

AKROMID®

B28 GM 5/25 FR black (7492)

PA6 (GF5+GB25) FR(40)

AKROMID® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength

Modulus

5.000MPa

Strength

55MPa

Impact

30kJ/m²

AKROMID® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength

142434480

AKROMID®

Preliminary

B28 GF 15 natural (6940)PA6 GF 15

AKROMID B28 GF 15 natural (6940) is a 15% glass fibre reinforced, easy flowing PA6. Due to its very good flowability, this grade has a good surface. It complies with the bus fire standard ECE R 118.03 annex 6, 7, 8 and is suitable for panels and components in luggage racks where medium stiffness and strength is required. The material is easy to colour.

Features

easy flow
public transportation

Regulatory

ece11803

Properties

Modulus

5.300MPa

Strength

120MPa

Impact

39kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
5300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
210 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
39 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Bus

ECE 118

Appendix 6, 7, 8

General properties

Density

ISO 1183

23°C
1,23 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.