AKROMID®

B3 GF 30 1 GIT black (4598)

PA6 GF30

AKROMID® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

Modulus

9.500MPa

Strength

175MPa

Impact

NA

AKROMID® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

AKROMID®

B3 GM 10/20 1 L black (4646)

PA6+PP (GF10+GB20)

AKROMID® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride

Modulus

5.100MPa

Strength

88MPa

Impact

46kJ/m²

AKROMID® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride

AKROMID®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/m²

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

AKROMID®

A3 GF 30 6 black (6736)

PA66 GF30

AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

AKROMID®

B+ GF 30 6 black (7387)

PA6 GF30

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

9.500MPa

Strength

180MPa

Impact

86kJ/m²

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

AKROMID®

C3 5 S3 black (8029)

PA66+PA6

AKROMID® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems

PRECITE®

Preliminary

P3 GF 30 4 black (8333)

PBT-I GF30

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.000MPa

Strength

115MPa

Impact

65kJ/m²

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

140414280

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)PA6 (GF15+GB15) FR(40)

AKROMID® B28 GM 15/15 1 FR black (8750) is a flame retardant PA6 reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens and red phosphorus. Due to its good flowability, it is characterised by easy processability as well as good surface properties. The product is suitable for enclosure applications in the E&E industry due to its low warpage, high stiffness and strength. This grade is excellent for laser marking.

Features

flame retardant
laser markable
surface modified
low warpage
easy flow
E&E

Regulatory

ul

Properties

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8400 MPa
5200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
105 MPa
65 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,7 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
45 kJ/m²
40 kJ/m²
40 kJ/m²
35 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
102 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
775 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,44 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,65 - 0,85 %
0,75 - 0,95 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more