AKROMIDĀ®

B3 GF 30 1 GIT black (4598)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

Modulus

9.500MPa

Strength

175MPa

Impact

NA

AKROMIDĀ® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

AKROMIDĀ®

B3 GM 10/20 1 L black (4646)

PA6+PP (GF10+GB20)

AKROMIDĀ® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride

Modulus

5.100MPa

Strength

88MPa

Impact

46kJ/mĀ²

AKROMIDĀ® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride

AKROMIDĀ®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/mĀ²

AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

AKROMIDĀ®

A3 GF 30 6 black (6736)

PA66 GF30

AKROMIDĀ® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/mĀ²

AKROMIDĀ® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

AKROMIDĀ®

B+ GF 30 6 black (7387)

PA6 GF30

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

9.500MPa

Strength

180MPa

Impact

86kJ/mĀ²

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

AKROMIDĀ®

C3 5 S3 black (8029)

PA66+PA6

AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems

PRECITEĀ®

Preliminary

P3 GF 30 4 black (8333)

PBT-I GF30

PRECITEĀ®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.000MPa

Strength

115MPa

Impact

65kJ/mĀ²

PRECITEĀ®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

140414280

AKROMIDĀ®

C28 GF 25 FRT grey (8331)PA-Blend

AKROMIDĀ® C28 GF 25 FRT grey (8331) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend, colored in grey similar to NCS S 3000 N. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications and certified to EN 45545-2 R6 and EN 45545-2 R1. To achieve an excellent surface quality a mould temperature of at least 120Ā°C is necessary.

Features

flame retardant
surface modified
easy flow
public transportation

Regulatory

en45545-2

Properties

Modulus

10.800MPa

Strength

140MPa

Impact

47kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,0 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
47 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
238 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,2 10ā»ā“/K
0,66 10ā»ā“/K

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

Burning rate 5V

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
5VA Class
5VA Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 Ā°C
960 Ā°C
960 Ā°C
960 Ā°C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 Ā°C
800 Ā°C
800 Ā°C
850 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Train

EN 45545-2

R1/6/7 HL2

General properties

Density

ISO 1183

23Ā°C
1,44 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,9 - 1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
< 0,2 %
0,1 - 0,3 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more