AKROMID^®

B3 GFM 10/20 1 grey (4561)

PA6 (GF10+MD20)

AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

Modulus

5.800MPa

Strength

100MPa

Impact

50kJ/m²

AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

AKROTEK^®

PK-HM natural (4773)

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMID^®

B3 ICF 10 black (5118)

PA6 CF10

AKROMID® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/m²

AKROMID® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROLOY^®

PA LGF 50 natural (5504)

PA66+PA6I/6T LGF50

AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance

Modulus

19.000MPa

Strength

290MPa

Impact

100kJ/m²

AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance

PRECITE^®

P3 GF 50 natural (6944)

PBT GF 50

PRECITE® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

17.000MPa

Strength

185MPa

Impact

60kJ/m²

AKROMID^®

C3 1 FR orange (7470)

PA66+PA6 FR(30)

AKROMID® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

Modulus

3.500MPa

Strength

76MPa

Impact

AKROMID® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

AKROMID^®

B28 GF 15 1 S3 black (7514)

PA6-I GF15

AKROMID® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

Modulus

5.000MPa

Strength

110MPa

Impact

70kJ/m²

AKROMID® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

1 40 41 4280

AKROMID^®

A3 GF 30 FR black (7751)PA66 GF30 FR(40)

AKROMID® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.

Features

flame retardant

Regulatory

Properties

Modulus

10.500MPa

Strength

150MPa

Impact

67kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

10500 MPa

7600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

150 MPa

107 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

2,7 %

3,9 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

11500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

230 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

67 kJ/m²

70 kJ/m²

61 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

10 kJ/m²

13 kJ/m²

9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

246 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

261 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

262 °C

Ball pressure test

IEC 60695-10-2

> 210 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

750 °C

775 °C

HWI

UL 746A

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

0 PLC

HAI

UL 746A

0,4 mm Wall thickness

0,8 mm Wall thickness

1,6 mm Wall thickness

3,2 mm Wall thickness

0 PLC

General properties

Density

ISO 1183

23°C

1,39 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,9 - 2,1 %

Water absorption

ISO 62

23°C, saturated

5,3 - 5,6 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,7 - 0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.

conditioned

10¹⁵ Ω x cm

10¹³ Ω x cm

Comparative tracking index

IEC 60112

Test liquid A

600 V

Comparative tracking index

ASTM D3638

0 PLC

Dielectric strength

IEC 60243

3 mm

15 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

1 kV

High voltage arc tracking rate (HVTR)

UL 746A

1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

6 PLC

Rheological Properties

Flowability

AKRO

1 mm Thickness

2 mm Thickness

140 mm

440 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

A3 GF 30 FR black (7751)PA66 GF30 FR(40)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Ball pressure test

Flammability

Burning rate

GWFI

GWIT

HWI

HAI

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Comparative tracking index

Comparative tracking index

Dielectric strength

Inclined-Plane Tracking, IPT

High voltage arc tracking rate (HVTR)

High Volt, Low Current Arc Resistance

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

Find the right compound

A3 GF 30 FR black (7751).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA66 GF30 FR(40)

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Melting temperature

Ball pressure test

Flammability

Burning rate

GWFI

GWIT

HWI

HAI

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Comparative tracking index

Comparative tracking index

Dielectric strength

Inclined-Plane Tracking, IPT

High voltage arc tracking rate (HVTR)

High Volt, Low Current Arc Resistance

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

A3 GF 30 FR black (7751)PA66 GF30 FR(40)