HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

C3 GFM 15/25 1 black (6653)

PA66+PA6 (GF15+M25)

AKROMID® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/m²

AKROMID® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability

AKROMID®

B3 GK 50 natural (3690)

PA6 GB50

AKROMID® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/m²

AKROMID® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

AKROMID®

B3 ICF 10 black (5118)

PA6 CF10

AKROMID® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/m²

AKROMID® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROMID®

UL

A3 GF 30 FR black (7751)

PA66 GF30 FR(40)

AKROMID® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.

Modulus

10.500MPa

Strength

150MPa

Impact

67kJ/m²

AKROMID® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.

AKROMID®

B28 GF 15 1 S3 black (7514)

PA6-I GF15

AKROMID® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

Modulus

5.000MPa

Strength

110MPa

Impact

70kJ/m²

AKROMID® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

PRECITE®

Preliminary

P3 GF 30 4 black (8333)

PBT-I GF30

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.000MPa

Strength

115MPa

Impact

65kJ/m²

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

140414280

AKROMID®

B3 GF 40 5 black (7286)PA6 GF40

AKROMID® B3 GF 40 5 black (7286) is a 40% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is high heat stabilised and therefore perfectly suitable for technical parts which are used at elevated temperatures in industrial engineering and in the automotive industry. As successor AKROMID® B3 GF 40 5 black (8636) was delevoped, to meet the stringent UV stability requirements for outdoor applications.

Features

heat stabilised 160

Properties

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12500 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
129 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12300 MPa
7500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
310 MPa
200 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,3 %
5,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
95 kJ/m²
103 kJ/m²
92 kJ/m²
96 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
16 kJ/m²
24 kJ/m²
13 kJ/m²
14 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,45 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

Flowability

AKRO

2 mm Thickness
480 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more