AKROMIDĀ®

B3 GFM 10/20 1 grey (4561)

PA6 (GF10+MD20)

AKROMIDĀ® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

Modulus

5.800MPa

Strength

100MPa

Impact

50kJ/mĀ²

AKROMIDĀ® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

AKROTEKĀ®

PK-HM natural (4773)

PK

AKROTEKĀ® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMIDĀ®

B3 ICF 10 black (5118)

PA6 CF10

AKROMIDĀ® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

AKROMIDĀ® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROLOYĀ®

PA LGF 50 natural (5504)

PA66+PA6I/6T LGF50

AKROLOYĀ® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance

Modulus

19.000MPa

Strength

290MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance

PRECITEĀ®

P3 GF 50 natural (6944)

PBT GF 50

PRECITEĀ® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

17.000MPa

Strength

185MPa

Impact

60kJ/mĀ²

PRECITEĀ® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMIDĀ®

UL

C3 1 FR orange (7470)

PA66+PA6 FR(30)

AKROMIDĀ® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

Modulus

3.500MPa

Strength

76MPa

Impact

NA

AKROMIDĀ® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

AKROMIDĀ®

B28 GF 15 1 S3 black (7514)

PA6-I GF15

AKROMIDĀ® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

Modulus

5.000MPa

Strength

110MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

140414280

AKROMIDĀ®

B3 GF 60 1 black (4644)PA6 GF60

AKROMIDĀ® B3 GF 60 1 black (4644) is a 60% glass fiber reinforced, heat stabilised polyamide 6. It is characterised by an improved flowability compared to a standard PA 6 GF 60. Furthermore, the material impresses with its high stiffness and strength. It is therefore perfectly suitable for technical applications in industrial engineering and in the automotive industry.

Features

heat stabilised 130
easy flow

Properties

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
21000 MPa
13500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
19000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
370 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
90 kJ/mĀ²
95 kJ/mĀ²
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
20 kJ/mĀ²
25 kJ/mĀ²
20 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,13 10ā»ā“/K
0,60 10ā»ā“/K

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,7 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,9 - 1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Rheological Properties

Flowability

AKRO

2 mm Thickness
320 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.