Description

AKROMIDĀ®

B3 GF 30 1 GIT black (4598)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

Modulus

9.500MPa

Strength

175MPa

Impact

NA

AKROMIDĀ® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

AKROMIDĀ®

B3 GM 10/20 1 L black (4646)

PA6+PP (GF10+GB20)

AKROMIDĀ® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride

Modulus

5.100MPa

Strength

88MPa

Impact

46kJ/mĀ²

AKROMIDĀ® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride

AKROMIDĀ®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/mĀ²

AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

AKROMIDĀ®

A3 GF 30 6 black (6736)

PA66 GF30

AKROMIDĀ® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/mĀ²

AKROMIDĀ® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

AKROMIDĀ®

B+ GF 30 6 black (7387)

PA6 GF30

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

9.500MPa

Strength

180MPa

Impact

86kJ/mĀ²

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

AKROMIDĀ®

C3 5 S3 black (8029)

PA66+PA6

AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems

PRECITEĀ®

Preliminary

P3 GF 30 4 black (8333)

PBT-I GF30

PRECITEĀ®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.000MPa

Strength

115MPa

Impact

65kJ/mĀ²

PRECITEĀ®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

140414280

AKROMIDĀ®

B3 GF 25 1 L black (4637)PA6+PP GF25

AKROMIDĀ® B3 GF 25 1 L black (4637) is a PA6/PP-blend with reduced density compared to standard PA6 with 25% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 25 1 L black (4637) is particularly superior to calcium chloride (CaClā‚‚).

Features

heat stabilised 130
reduced density

Properties

Modulus

7.500MPa

Strength

135MPa

Impact

68kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
5600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
88 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,3 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
68 kJ/mĀ²
58 kJ/mĀ²
67 kJ/mĀ²
54 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
15 kJ/mĀ²
15 kJ/mĀ²
13 kJ/mĀ²
10 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
198 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 Ā°C
725 Ā°C
750 Ā°C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 Ā°C
750 Ā°C
775 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,22 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,55 - 0,75 %

Rheological Properties

MVR

ISO 1133

275Ā°C/5kg
10 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.