AKROMIDĀ®
B3 GF 30 1 GIT black (4598)
PA6 GF30
AKROMIDĀ® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.
9.500MPa
175MPa
NA
AKROMIDĀ® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.
AKROMIDĀ®
B3 GM 10/20 1 L black (4646)
PA6+PP (GF10+GB20)
AKROMIDĀ® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride
5.100MPa
88MPa
46kJ/mĀ²
AKROMIDĀ® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride
AKROMIDĀ®
D3 CGM 15/20 S1 black (6284)
PA612 (CF15+GF20)
AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity
13.500MPa
145MPa
80kJ/mĀ²
AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity
AKROMIDĀ®
A3 GF 30 6 black (6736)
PA66 GF30
AKROMIDĀ® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry
10.000MPa
200MPa
75kJ/mĀ²
AKROMIDĀ® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry
AKROMIDĀ®
B+ GF 30 6 black (7387)
PA6 GF30
Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
9.500MPa
180MPa
86kJ/mĀ²
Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds
AKROMIDĀ®
C3 5 S3 black (8029)
PA66+PA6
AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems
2.500MPa
65MPa
180kJ/mĀ²
AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems
PRECITEĀ®
P3 GF 30 4 black (8333)
PBT-I GF30
PRECITEĀ®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.
9.000MPa
115MPa
65kJ/mĀ²
PRECITEĀ®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.
AKROMIDĀ®
B3 GF 30 1 HU LA black (2862)PA6 GF30
AKROMIDĀ® B3 GF 30 1 HU LA black (2862) is a 30% glass fibre reinforced, heat ageing resistant polyamide 6 with high rigidity and strength. This UL94 HB listed grade is suitable for technical components in mechanical engineering and the automotive industry. The material is laser markable.
Features
Regulatory
Properties
10.300MPa
185MPa
95kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
UV Exposure and Water Immersion
UL 746C
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Electrical Properties
Surface resistivity
DIN EN 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.