AKROMID®
T9 GF 50 natural (8334)
PPA GF50
AKROMID® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
16.500MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
B3 GF 50 1 natural (2531)
PA6 GF50
AKROMID® B3 GF 50 1 natural (2531) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
17.000MPa
230MPa
100kJ/m²
AKROMID® B3 GF 50 1 natural (2531) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B28 GF 60 9 black (4662)
PA6 GF60
AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
21.000MPa
250MPa
90kJ/m²
AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
PRECITE®
K GF 50 natural (7435)
PBT-PET- GF 50
PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.
20.000MPa
175MPa
60kJ/m²
PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.
AKROMID®
A3 GF 30 FR black (7751)
PA66 GF30 FR(40)
AKROMID® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.
10.500MPa
150MPa
67kJ/m²
AKROMID® A3 GF 30 FR black (7751) is an at UL in all colors listed PA66 with 30% glass-fibers and flame retardant free of halogens and red phosphorus. The color is similar to RAL 9005.
AKROMID®
C28 M 30 6 black (7934)
PA66+PA6 MD30
AKROMID® C28 M 30 6 black (7934) is a 30% mineral filled, high heat stabilized polyamid 6.6/6 with very good surface low warpage and easy flow.
6.000MPa
70MPa
30kJ/m²
AKROMID® C28 M 30 6 black (7934) is a 30% mineral filled, high heat stabilized polyamid 6.6/6 with very good surface low warpage and easy flow.
AKROMID®
B3 GM 15/15 natural (3079)
PA6 (GF15+GB15)
AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color
7.200MPa
130MPa
64kJ/m²
AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color
AKROMID®
C28 GFM 10/20 5 XTC black (7367)PA66+PA6 (GF10+MD20)
AKROMID® C28 GFM 10/20 5 XTC black (7367) is a 10% glass fiber and 20% mineral reinforced, easy flowing polyamide 6.6/6 blend. It is characterised by excellent temperature resistance as well as a very high surface quality. Furthermore, the material impresses with low warpage, resulting in high dimensional stability. It is therefore perfectly suitable for parts in industrial engineering and in the automotive industry, e.g. under the hood, which are exposed to high temperatures.
Features
Properties
9.500MPa
120MPa
40kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.