A3 GF 30 FR natural (7087)

PA66 GF30 FR(40)

AKROMIDĀ® A3 GF 30 FR natural (7087) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors.

Modulus

10.000MPa

Strength

140MPa

Impact

61kJ/mĀ²

AKROMIDĀ® A3 GF 30 FR natural (7087) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors.

AKROMIDĀ®

UL

B3 GF 30 FR black (7459)

PA6 GF30 FR(40)

AKROMIDĀ® B3 GF 30 FR black (7459) is an at UL in all colors listed PA6 with 30% glass-fibers and flame retardant free of halogens and red phosphorus.

Modulus

10.800MPa

Strength

135MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 30 FR black (7459) is an at UL in all colors listed PA6 with 30% glass-fibers and flame retardant free of halogens and red phosphorus.

AKROMIDĀ®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMIDĀ® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

AKROMIDĀ®

B3 GF 30 1 GIT black (4598)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

Modulus

9.500MPa

Strength

175MPa

Impact

NA

AKROMIDĀ® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

AKROMIDĀ®

B3 GF 60 1 black (4644)

PA6 GF60

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

AKROMIDĀ®

UL
Preliminary

A3 GF 60 HU natural (6452)

PA66 GF60

AKROMIDĀ® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color

Modulus

20.500MPa

Strength

270MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color

AKROMIDĀ®

B3 CGM 6/20 black (4362)

PA6 (CF6+GF20)

AKROMIDĀ® B3 CGM 6/20 black (4362) - PA 6, 20% glass fiber reinforced, 6% carbon fiber reinforced, heat stabilized, electrical conductivity

Modulus

11.000MPa

Strength

175MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 CGM 6/20 black (4362) - PA 6, 20% glass fiber reinforced, 6% carbon fiber reinforced, heat stabilized, electrical conductivity

139404180

AKROMIDĀ®

A3 ICF 30 5 black (6495)PA66 CF30

AKROMIDĀ® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties

Features

heat stabilised 230

Properties

Modulus

23.000MPa

Strength

235MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
23000 MPa
14500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
235 MPa
165 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,8 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
22000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
370 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
50 kJ/mĀ²
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
8 kJ/mĀ²
11 kJ/mĀ²
6 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,06 10ā»ā“/K
0,72 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,27 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
104 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more