Select your fitting and find the right compound for your intend
AKROMID®
B28 GF 30 1 black (4962)
PA6 GF30
AKROMID® B28 GF 30 1 black (4962) is a 30% glass fibre reinforced, heat stabilised and easy flowing polyamide 6 with high stiffness and strength.
9.500MPa
170MPa
75kJ/m²
AKROMID® B28 GF 30 1 black (4962) is a 30% glass fibre reinforced, heat stabilised and easy flowing polyamide 6 with high stiffness and strength.
AKROMID®
A3 ICF 40 black (5116)
PA66 CF40
AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
33.000MPa
270MPa
60kJ/m²
AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROLOY®
PA LGF 50 natural (5504)
PA66+PA6I/6T LGF50
AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance
19.000MPa
290MPa
100kJ/m²
AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance
AKROMID®
B28 GF 30 6 LT black (6931)
PA6 GF30
AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent
9.800MPa
185MPa
90kJ/m²
AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent
AKROMID®
T9 GF 50 natural (8334)
PPA GF50
AKROMID® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
16.500MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
B28 GF 60 9 black (4662)
PA6 GF60
AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
21.000MPa
250MPa
90kJ/m²
AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
AKROLOY®
PA ICF 20 black (5268)
PA66 + PA6I/6T CF20
AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
17.000MPa
200MPa
45kJ/m²
AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROLOY®
AKROLOY® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
Properties
21.000MPa
280MPa
100kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 1110
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.