Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITE®

Preliminary

K GF 50 natural (7435)

PBT-PET- GF 50

PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.

Modulus

20.000MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.

AKROMID®

UL

C3 1 FR orange (7470)

PA66+PA6 FR(30)

AKROMID® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

Modulus

3.500MPa

Strength

76MPa

Impact

NA

AKROMID® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

AKROMID®

B3 GM 15/15 natural (3079)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

AKROMID®

C3 GF 30 5 XTC natural (4499)

PA66 + PA6 GF 30

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

AKROMID®

A3 ICF 40 black (5116)

PA66 CF40

AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

33.000MPa

Strength

270MPa

Impact

60kJ/m²

AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROLOY®

Preliminary

PA GF 30 natural (6412)

PA66+PA6I/6T GF30

AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

10.200MPa

Strength

200MPa

Impact

70kJ/m²

AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROMID®

UL

B3 GF 30 FR orange (7857)

PA6 GF 30 FR(40)

AKROMID® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

Modulus

10.500MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

138394080

AKROMID®

UL

B3 1 FR black (6580)PA6 FR(30)

AKROMID® B3 1 FR black (6580) is an unreinforced, flame retardant and heat stabilised PA6. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade meets the requirements for public transportation (EN 45545-2) and is also suitable for housing, fasteners and cable connectors in the E&E markets.

Features

heat stabilised 130
flame retardant
surface modified
easy flow
E&E
public transportation

Regulatory

en45545-2ul

Properties

Modulus

3.600MPa

Strength

75MPa

Impact

78kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
75 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 10 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3500 MPa
1300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
115 MPa
45 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
78
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
4,5 kJ/m²
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,78 10⁻⁴/K
0,78 10⁻⁴/K

Flammability

Burning rate

UL 94

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 °C
750 °C
750 °C
775 °C

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
4 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Oxygen index

ISO 4589-2

> 32 %

Protection Train

EN 45545-2

R22/R23/24/26 HL3

General properties

Density

ISO 1183

23°C
1,19 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,3 - 2,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,9 - 1,1 %
1,0 - 1,2 %

Electrical Properties

Comparative tracking index

IEC 60112

UL
Test liquid A
> 600 V

Dielectric strength

IEC 60243

UL
3 mm
10 kV/mm

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
200 mm
500 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.