AKROMID®

UL

B3 GF 30 FR orange (7857)

PA6 GF 30 FR(40)

AKROMID® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

Modulus

10.500MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

AKROMID®

UL

C3 1 FR orange (7470)

PA66+PA6 FR(30)

AKROMID® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

Modulus

3.500MPa

Strength

76MPa

Impact

NA

AKROMID® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

AKROLOY®

Preliminary

PA CF 40 1 black (8392)

PA66 + PA6I/6T CF40

AKROLOY® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

30.300MPa

Strength

300MPa

Impact

70kJ/m²

AKROLOY® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B3 GF 30 black (2493)

PA6 GF30

AKROMID® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

AKROMID®

A3 GF 30 1 L black (4436)

PA66+PP GF30

AKROMID® A3 GF 30 1 L black (4436) - PA6.6/PP-Blend glass fibre reinforced with lower density, cost reduced, zinc chloride

Modulus

8.400MPa

Strength

150MPa

Impact

77kJ/m²

AKROMID® A3 GF 30 1 L black (4436) - PA6.6/PP-Blend glass fibre reinforced with lower density, cost reduced, zinc chloride

AKROMID®

C3 GF 30 5 XTC natural (4499)

PA66 + PA6 GF 30

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

137383980

AKROMID®

Preliminary
Internal

NEXT 5.6 3 GF 35 9 FR natural (8401)PA56 GF35 FR(40)

AKROMID® NEXT 5.6 3 GF 35 9 FR natural (8401) is a partially bio-based and flame retardant PA 5.6 and meets the requirement according to UL94 V0 @ 1.6 mm. The flame-retardant system is free of red phosphorus and halogens. PA 5.6 is a HMD-free (hexamethylenediamine) alternative to PA 6.6. With 35% glass fibre reinforcement, the material is suitable for components with high strength requirements for E&E and E-Mobility, such as busbar supports, switches, terminal strips and connector housings.

Features

Bio-based
heat stabilised 130
flame retardant
E&E

Properties

Modulus

12.000MPa

Strength

160MPa

Impact

71kJ/m²

Sustainability

Biobased carbon content

35 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12500 MPa
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
255 MPa
160 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
4,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
71 kJ/m²
70 kJ/m²
69 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
15 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
254 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
900 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
725 °C
725 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,43 g/cm³

Water absorption

ISO 62

23°C, saturated
2,0 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more