AKROLOY®

PA GF 50 8 black (6732)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS

Modulus

17.500MPa

Strength

260MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS

PRECITE®

P3 ICF 20 black (6947)

PBT CF20

PRECITE® P3 ICF 20 black (6947) is a 20% carbon fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as low Density and good tribological properties

Modulus

16.000MPa

Strength

150MPa

Impact

50kJ/m²

PRECITE® P3 ICF 20 black (6947) is a 20% carbon fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as low Density and good tribological properties

AKROMID®

UL

C3 1 FR natural (8050)

PA66+PA6 FR(30)

AKROMID® C3 1 FR natural (8050) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, very good flowability, public transportation, new mobility.

Modulus

3.600MPa

Strength

77MPa

Impact

100kJ/m²

AKROMID® C3 1 FR natural (8050) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, very good flowability, public transportation, new mobility.

AKROLOY®

PA ICF 40 black (5270)

PA66+PA6I/6T CF40

AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

32.000MPa

Strength

250MPa

Impact

55kJ/m²

AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/m²

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

AKROMID®

C3 GFM 15/25 1 black (6653)

PA66+PA6 (GF15+M25)

AKROMID® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/m²

AKROMID® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability

AKROMID®

B28 GF 30 6 LT black (6931)

PA6 GF30

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/m²

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

137383980

AKROMID®

B3 GM 10/20 1 L black (4646)PA6+PP (GF10+GB20)

AKROMID® B3 GM 10/20 1 L black (4646) is a PA6/PP-blend with reduced density compared to standard PA6 GM 10/20. With 10% glass fibre reinforcement and 20% glass bead filling the material is suitable for components with average strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMID® B3 GM 10/20 1 L black (4646) is particularly superior to calcium chloride (CaCl₂).

Features

heat stabilised 130
reduced density

Properties

Modulus

5.100MPa

Strength

88MPa

Impact

46kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
5100 MPa
3300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
88 MPa
55 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,4 %
6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
130 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
46 kJ/m²
44 kJ/m²
43 kJ/m²
42 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
7 kJ/m²
9 kJ/m²
4 kJ/m²
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
165 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
208 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,26 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
18 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more