AKROMID®

B3 GF 50 1 natural (2531)

PA6 GF50

AKROMID® B3 GF 50 1 natural (2531) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 1 natural (2531) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 ICF 20 black (5102)

PA66 CF20

AKROMID® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

16.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROMID® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

PRECITE®

P3 ICF 20 black (6947)

PBT CF20

PRECITE® P3 ICF 20 black (6947) is a 20% carbon fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as low Density and good tribological properties

Modulus

16.000MPa

Strength

150MPa

Impact

50kJ/m²

PRECITE® P3 ICF 20 black (6947) is a 20% carbon fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as low Density and good tribological properties

AKROMID®

B+ GF 30 6 black (7387)

PA6 GF30

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

9.500MPa

Strength

180MPa

Impact

86kJ/m²

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

AKROMID®

UL

B3 GF 30 FR black (7459)

PA6 GF30 FR(40)

AKROMID® B3 GF 30 FR black (7459) is an at UL in all colors listed PA6 with 30% glass-fibers and flame retardant free of halogens and red phosphorus.

Modulus

10.800MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® B3 GF 30 FR black (7459) is an at UL in all colors listed PA6 with 30% glass-fibers and flame retardant free of halogens and red phosphorus.

AKROMID®

A3 GF 30 1 S3 black (3502)

PA66-I GF30

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

Modulus

8.000MPa

Strength

170MPa

Impact

100kJ/m²

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

137383980

AKROMID®

B3 GFM 10/20 1 black (2017)PA6 (GF10+M20)

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

Features

heat stabilised 130
surface modified
low warpage

Properties

Modulus

6.200MPa

Strength

110MPa

Impact

40kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
170 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
5,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
40 kJ/m²
40 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
3 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
185 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
215 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
55 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,6 %
0,8 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
170 mm
390 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more