Description

AKROMID®

B28 GF 60 9 black (4662)

PA6 GF60

AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/m²

AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

AKROMID®

A3 ICF 40 black (5116)

PA66 CF40

AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Modulus

33.000MPa

Strength

270MPa

Impact

60kJ/m²

AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

AKROMID®

A3 GF 30 6 black (6736)

PA66 GF30

AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

AKROMID®

B28 GF 30 6 LT black (6931)

PA6 GF30

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/m²

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

PRECITE®

Preliminary

K GF 50 natural (7435)

PBT-PET- GF 50

PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.

Modulus

20.000MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.

AKROMID®

UL

B3 GF 30 FR black (7459)

PA6 GF30 FR(40)

AKROMID® B3 GF 30 FR black (7459) is an at UL in all colors listed PA6 with 30% glass-fibers and flame retardant free of halogens and red phosphorus.

Modulus

10.800MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® B3 GF 30 FR black (7459) is an at UL in all colors listed PA6 with 30% glass-fibers and flame retardant free of halogens and red phosphorus.

136373880

AKROMID®

B3 GF 45 1 black (3851)PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Features

heat stabilised 130

Properties

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14500 MPa
8500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
8,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
13000 MPa
7500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
315 MPa
200 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
4,5 %
6,7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
110 kJ/m²
108 kJ/m²
95 kJ/m²
108 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
20 kJ/m²
25 kJ/m²
16 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
145 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,5 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.