AKROMID®

B3 GFM 10/20 1 grey (4561)

PA6 (GF10+MD20)

AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

Modulus

5.800MPa

Strength

100MPa

Impact

50kJ/m²

AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

AKROLOY®

PA ICF 40 black (5270)

PA66+PA6I/6T CF40

AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

32.000MPa

Strength

250MPa

Impact

55kJ/m²

AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROLOY®

PA ICF 20 black (5268)

PA66 + PA6I/6T CF20

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

17.000MPa

Strength

200MPa

Impact

45kJ/m²

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

A3 GF 50 1 EN black (5737)

PA66 GF50

AKROMID® A3 GF 50 1 EN black (5737) - 50% glass fiber reinforced PA 6.6, electrically neutral and heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 EN black (5737) - 50% glass fiber reinforced PA 6.6, electrically neutral and heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOY®

PA GF 50 8 black (6732)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS

Modulus

17.500MPa

Strength

260MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS

PRECITE®

P3 GF 50 natural (6944)

PBT GF 50

PRECITE® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

17.000MPa

Strength

185MPa

Impact

60kJ/m²

PRECITE® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMID®

B3 GF 30 RM-M natural (3291)

PA6 + X GF30

AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

135363780

AKROMID®

C28 GF 25 FRT grey (8133)PA-Blend

AKROMID® C28 GF 25 FRT grey (8133) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend, colored in grey similar to RAL 7011. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications and certified to EN 45545-2 R6 and EN 45545-2 R1. To achieve an excellent surface quality a mould temperature of at least 120°C is necessary.

Features

flame retardant
surface modified
easy flow
public transportation

Regulatory

en45545-2

Properties

Modulus

11.000MPa

Strength

150MPa

Impact

Na

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,1 %

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 °C
800 °C
800 °C
850 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Train

EN 45545-2

R1/6/7 HL2

General properties

Density

ISO 1183

23°C
1,44 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,9 - 1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
< 0,2 %
0,1 - 0,3 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more