Description

AKROMID®

B3 GFM 10/20 1 grey (4561)

PA6 (GF10+MD20)

AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

Modulus

5.800MPa

Strength

100MPa

Impact

50kJ/m²

AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

AKROLOY®

PA ICF 40 black (5270)

PA66+PA6I/6T CF40

AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

32.000MPa

Strength

250MPa

Impact

55kJ/m²

AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROLOY®

PA ICF 20 black (5268)

PA66 + PA6I/6T CF20

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

17.000MPa

Strength

200MPa

Impact

45kJ/m²

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

A3 GF 50 1 EN black (5737)

PA66 GF50

AKROMID® A3 GF 50 1 EN black (5737) - 50% glass fiber reinforced PA 6.6, electrically neutral and heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 EN black (5737) - 50% glass fiber reinforced PA 6.6, electrically neutral and heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOY®

PA GF 50 8 black (6732)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS

Modulus

17.500MPa

Strength

260MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS

PRECITE®

P3 GF 50 natural (6944)

PBT GF 50

PRECITE® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

17.000MPa

Strength

185MPa

Impact

60kJ/m²

PRECITE® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMID®

B3 GF 30 RM-M natural (3291)

PA6 + X GF30

AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

135363780

AKROMID®

A3 1 L black (4652)PA66 + PP

AKROMID® A3 1 L black (4652) is an unreinforced PA6.6/PP-blend with reduced density compared to standard PA6.6. The material can be used where weight and cost reduction is required.

Features

heat stabilised 130
reduced density

Properties

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
54 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
30 %
> 50 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
6,5 kJ/m²
12 kJ/m²
5 kJ/m²
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
65 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
800 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,04 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
2,5 %
1,8 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
29 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more