Description

AKROMID®

B3 GM 15/15 natural (3079)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

AKROMID®

B3 GF 15 1 black (2482)

PA6 GF15

AKROMID® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/m²

AKROMID® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

AKROLOY®

PA ICF 20 black (5268)

PA66 + PA6I/6T CF20

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

17.000MPa

Strength

200MPa

Impact

45kJ/m²

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

AKROLOY®

PA ICF 40 black (5270)

PA66+PA6I/6T CF40

AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

32.000MPa

Strength

250MPa

Impact

55kJ/m²

AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B3 GFM 10/20 1 grey (4561)

PA6 (GF10+MD20)

AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

Modulus

5.800MPa

Strength

100MPa

Impact

50kJ/m²

AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability

135363780

AKROMID®

Internal

S3 GF 50 1 natural (3533)PA610 GF50

AKROMID® S3 GF 50 1 natural (3533) is a 50% glass fibre reinforced, heat stabilised polyamide 6.10 with very high stiffness and strength as well as lower moisture absorption, high chemical resistance and light inherent color.

Features

heat stabilised 130
reduced moisture

Properties

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

61 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
14500 MPa
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
310 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
105 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
20 kJ/m²
16 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,51 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more