AKROMID®
C3 GF 30 5 XTC natural (4499)
PA66 + PA6 GF 30
AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.
9.500MPa
185MPa
95kJ/m²
AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.
AKROMID®
B3 ICF 30 black (5119)
PA6 CF30
AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
23.000MPa
200MPa
55kJ/m²
AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
AKROLOY®
PA ICF 40 black (5270)
PA66+PA6I/6T CF40
AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
32.000MPa
250MPa
55kJ/m²
AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced, UV-stabilised, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROLOY®
PA LGF 50 natural (5504)
PA66+PA6I/6T LGF50
AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance
19.000MPa
290MPa
100kJ/m²
AKROLOY® PA LGF 50 natural (5504) - Semi-aromatic polyamide blend, 50% long glass fiber reinforced, low shrinkage, very good fatigue performance
AKROMID®
A3 GF 60 HU natural (6452)
PA66 GF60
AKROMID® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color
20.500MPa
270MPa
105kJ/m²
AKROMID® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color
AKROMID®
A3 GF 50 6 black (6860)
PA66 GF50
AKROMID® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
18.000MPa
250MPa
105kJ/m²
AKROMID® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 30 black (2493)
PA6 GF30
AKROMID® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
10.300MPa
185MPa
75kJ/m²
AKROMID® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GK 40 1 black (1804)PA66 GB40
AKROMID® A3 GK 40 1 black (1804) is a heat stabilised PA 6.6 filled with 40% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.
Features
Properties
5.500MPa
95MPa
25kJ/m²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.