AKROMID®

B3 GM 15/15 natural (3079)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

AKROMID®

B3 GF 40 1 L black (4581)

PA6 + PP GF40

AKROMID® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

11.000MPa

Strength

150MPa

Impact

70kJ/m²

AKROMID® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMID®

Preliminary

B25 GF 50 LA black (8280)

PA6 GF50

AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

15.500MPa

Strength

235MPa

Impact

100kJ/m²

AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

AKROMID®

B3 GF 15 1 black (2482)

PA6 GF15

AKROMID® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/m²

AKROMID® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

AKROMID®

A3 GM 20/10 S1 black (4817)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

AKROMID®

B28 GF 30 1 black (4962)

PA6 GF30

AKROMID® B28 GF 30 1 black (4962) is a 30% glass fibre reinforced, heat stabilised and easy flowing polyamide 6 with high stiffness and strength.

Modulus

9.500MPa

Strength

170MPa

Impact

75kJ/m²

AKROMID® B28 GF 30 1 black (4962) is a 30% glass fibre reinforced, heat stabilised and easy flowing polyamide 6 with high stiffness and strength.

AKROMID®

B3 ICF 30 black (5119)

PA6 CF30

AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

23.000MPa

Strength

200MPa

Impact

55kJ/m²

AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

133343580

PRECITE®

Preliminary

E GF 50 natural (7300)PET GF50

PRECITE® E GF 50 natural (7300) is a 50% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with very high stiffness and toughness even at elevated temperatures. Due to its low moisture absorption, this material is particularly dimensionally stable and therefore perfectly suitable for precision parts in the automotive, E&E and household goods industries, where a very good surface finish is required.

Features

surface modified
reduced moisture
E&E
metal substitution
Sports & leisure

Properties

Modulus

18.100MPa

Strength

220MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
18100 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
21000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
350 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
70 kJ/m²
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
14 kJ/m²
14 kJ/m²

Izod impact strength

ISO 180/1A

23°C | d.a.m.
54 kJ/m²

Izod notched impact strength

ISO 180/1A

23°C | d.a.m.
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
235 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
250 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,13 10⁻⁴/K
0,68 10⁻⁴/K

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,75 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more