AKROMID®

B+ GF 30 6 black (7387)

PA6 GF30

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

Modulus

9.500MPa

Strength

180MPa

Impact

86kJ/m²

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds

PRECITE®

Preliminary

K GF 50 natural (7435)

PBT-PET- GF 50

PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.

Modulus

20.000MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.

AKROMID®

C28 M 30 6 black (7934)

PA66+PA6 MD30

AKROMID® C28 M 30 6 black (7934) is a 30% mineral filled, high heat stabilized polyamid 6.6/6 with very good surface low warpage and easy flow.

Modulus

6.000MPa

Strength

70MPa

Impact

30kJ/m²

AKROMID® C28 M 30 6 black (7934) is a 30% mineral filled, high heat stabilized polyamid 6.6/6 with very good surface low warpage and easy flow.

AKROMID®

Preliminary

B25 GF 50 LA black (8280)

PA6 GF50

AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

15.500MPa

Strength

235MPa

Impact

100kJ/m²

AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

PRECITE®

Preliminary

P3 GF 30 4 black (8333)

PBT-I GF30

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.000MPa

Strength

115MPa

Impact

65kJ/m²

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROMID®

A3 GF 30 1 S3 black (3502)

PA66-I GF30

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

Modulus

8.000MPa

Strength

170MPa

Impact

100kJ/m²

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

AKROMID®

A3 GF 30 1 L black (4436)

PA66+PP GF30

AKROMID® A3 GF 30 1 L black (4436) - PA6.6/PP-Blend glass fibre reinforced with lower density, cost reduced, zinc chloride

Modulus

8.400MPa

Strength

150MPa

Impact

77kJ/m²

AKROMID® A3 GF 30 1 L black (4436) - PA6.6/PP-Blend glass fibre reinforced with lower density, cost reduced, zinc chloride

132333480

AKROMID®

A3 GK 40 1 black (1804)PA66 GB40

AKROMID® A3 GK 40 1 black (1804) is a heat stabilised PA 6.6 filled with 40% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

heat stabilised 130
low warpage

Properties

Modulus

5.500MPa

Strength

95MPa

Impact

25kJ/m²

Sustainability

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
5500 MPa
2600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
95 MPa
50 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
> 10 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
5800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
145 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
25 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
3 kJ/m²
5 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
120 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,44 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 %

Water absorption

ISO 62

23°C, saturated
5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,9 - 1,1 %
1,1 - 1,3 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1013 Ω

Comparative tracking index

IEC 60112

Test liquid A
500 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more