AKROMID®
B3 GK 50 black (2311)
PA6 GB50
AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage
5.700MPa
75MPa
42kJ/m²
AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage
AKROMID®
A3 GF 35 1 black (2269)
PA66 GF35
AKROMID® A3 GF 35 1 black (2269) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
11.600MPa
215MPa
92kJ/m²
AKROMID® A3 GF 35 1 black (2269) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GF 60 1 natural (2396)
PA66 GF60
AKROMID® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.
20.500MPa
260MPa
102kJ/m²
AKROMID® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.
AKROMID®
A3 GF 30 1 L black (4436)
PA66+PP GF30
AKROMID® A3 GF 30 1 L black (4436) - PA6.6/PP-Blend glass fibre reinforced with lower density, cost reduced, zinc chloride
8.400MPa
150MPa
77kJ/m²
AKROMID® A3 GF 30 1 L black (4436) - PA6.6/PP-Blend glass fibre reinforced with lower density, cost reduced, zinc chloride
AKROMID®
A28 GF 30 9 black (4915)
PA66 GF30
AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry
9.600MPa
200MPa
70kJ/m²
AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry
AKROMID®
C3 GFM 15/25 1 black (6653)
PA66+PA6 (GF15+M25)
AKROMID® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability
8.000MPa
120MPa
50kJ/m²
AKROMID® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability
AKROMID®
A3 GF 30 3 black (21005)
PA66 GF30
AKROMID® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry
10.000MPa
170MPa
55kJ/m²
AKROMID® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry
AKROTEK®
AKROTEK® PK-VM GF 15 8 black (6991) is a 15% glass fibre reinforced polyketone with average stiffness and strength. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances. Please note that the material is NOT suitable anymore for drinking water contact and does NOT meet the requirements according to KTW, DVGW W270, ACS, WRAS as well as NSF61.
Features
Regulatory
Properties
4.500MPa
95MPa
55kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.