HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

B3 GK 50 black (2311)

PA6 GB50

AKROMIDĀ® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/mĀ²

AKROMIDĀ® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage

AKROMIDĀ®

A3 GF 60 1 natural (2396)

PA66 GF60

AKROMIDĀ® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.

Modulus

20.500MPa

Strength

260MPa

Impact

102kJ/mĀ²

AKROMIDĀ® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.

AKROMIDĀ®

B3 GF 30 black (2493)

PA6 GF30

AKROMIDĀ® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

A3 GF 30 1 L black (4436)

PA66+PP GF30

AKROMIDĀ® A3 GF 30 1 L black (4436) - PA6.6/PP-Blend glass fibre reinforced with lower density, cost reduced, zinc chloride

Modulus

8.400MPa

Strength

150MPa

Impact

77kJ/mĀ²

AKROMIDĀ® A3 GF 30 1 L black (4436) - PA6.6/PP-Blend glass fibre reinforced with lower density, cost reduced, zinc chloride

AKROMIDĀ®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/mĀ²

AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

AKROLOYĀ®

Preliminary

PA GF 30 natural (6412)

PA66+PA6I/6T GF30

AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

10.200MPa

Strength

200MPa

Impact

70kJ/mĀ²

AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROMIDĀ®

C3 GFM 15/25 1 black (6653)

PA66+PA6 (GF15+M25)

AKROMIDĀ® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

AKROMIDĀ® C3 GFM 15/25 1 black (6653) is a glass fibre reinforced, mineral-filled, heat stabilised polyamide 6.6/6 blend for appealing surfaces and dimensional stability

131323380

AKROMIDĀ®

B3 GF 30 RM-M black (3016)PA6+X GF30

AKROMIDĀ® B3 GF 30 RM-M black (3016) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical changes in the conditioned state. It is therefore perfectly suitable for components where high dimensional stability is required, e.g. in sports and leisure.

Features

reduced moisture
Sports & leisure

Properties

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
7100 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
165 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,6 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
9600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,2 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
70 kJ/mĀ²
70 kJ/mĀ²
65 kJ/mĀ²
60 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
12 kJ/mĀ²
15 kJ/mĀ²
10 kJ/mĀ²
10 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,41 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 - 1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more