AKROMID®
B3 GK 50 black (2311)
PA6 GB50
AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage
5.700MPa
75MPa
42kJ/m²
AKROMID® B3 GK 50 black (2311) - PA 6, 50% glass beads reinforced, good surface, low warpage
AKROMID®
A3 GF 60 1 natural (2396)
PA66 GF60
AKROMID® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.
20.500MPa
260MPa
102kJ/m²
AKROMID® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.
AKROMID®
B3 GF 30 black (2493)
PA6 GF30
AKROMID® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
10.300MPa
185MPa
75kJ/m²
AKROMID® B3 GF 30 black (2493) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROMID®
B28 GF 60 9 black (4662)
PA6 GF60
AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
21.000MPa
250MPa
90kJ/m²
AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.
AKROLOY®
PA GF 50 8 black (6732)
PA66+PA6I/6T GF50
AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS
17.500MPa
260MPa
105kJ/m²
AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS
AKROMID®
B25 GF 50 LA black (8280)
PA6 GF50
AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
15.500MPa
235MPa
100kJ/m²
AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
AKROLOY®
PA CF 40 1 black (8392)
PA66 + PA6I/6T CF40
AKROLOY® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
30.300MPa
300MPa
70kJ/m²
AKROLOY® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROMID®
A3 GK 40 1 natural (1803)PA66 GB40
AKROMID® A3 GK 40 1 natural (1803) is a heat stabilised PA 6.6 filled with 40% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.
Features
Properties
5.500MPa
95MPa
25kJ/m²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.