PRECITE®

Preliminary

K GF 30 8 natural (7882)

PBT-PET- GF 30

PRECITE® K GF 30 8 natural (7882) - PBT/PET blend, 30% glass fibre, high stiffness, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

Modulus

10.000MPa

Strength

150MPa

Impact

70kJ/m²

PRECITE® K GF 30 8 natural (7882) - PBT/PET blend, 30% glass fibre, high stiffness, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)

PA6.6 GF30

AKROMID® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

AKROMID® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.

AKROMID®

UL
Preliminary

B28 GF 30 9 FR natural (8069)

PA6 GF 30 FR(40)

AKROMID® B28 GF 30 9 FR natural (8069) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

144MPa

Impact

80kJ/m²

AKROMID® B28 GF 30 9 FR natural (8069) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

AKROMID®

C28 GF 25 FRT grey (7560)

PA-Blend

AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

135MPa

Impact

60kJ/m²

AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

AKROMID®

B3 GF 50 1 black (2488)

PA6 GF50

AKROMID® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 40 1 LT black (5709)

PA66 GF40

AKROMID® A3 GF 40 1 LT black (5709) - 40% glass fiber reinforced PA 6.6, heat stabilised, laser transparent, for laser weldable components in the automotive and electronics industry

Modulus

13.000MPa

Strength

225MPa

Impact

100kJ/m²

AKROMID® A3 GF 40 1 LT black (5709) - 40% glass fiber reinforced PA 6.6, heat stabilised, laser transparent, for laser weldable components in the automotive and electronics industry

AKROMID®

B28 GF 50 9 natural (6570)

PA6 GF50

AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release

Modulus

17.000MPa

Strength

250MPa

Impact

115kJ/m²

AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release

127282980

AKROMID®

Internal

A3 GF 30 5 black (2180)PA66 GF30

AKROMID® A3 GF 30 5 black (2180) is a 30% glass fibre reinforced, high heat stabilised polyamide 6.6 with high stiffness and strength

Features

heat stabilised 160

Properties

Modulus

9.500MPa

Strength

190MPa

Impact

85kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9500 MPa
7000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
8500 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
280 MPa
210 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
85 kJ/m²
95 kJ/m²
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
10 kJ/m²
15 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
210 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,19 10⁻⁴/K
0,95 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,9 - 2,1 %

Water absorption

ISO 62

23°C, saturated
5,2 - 5,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more