AKROMID®

B28 GF 30 9 natural (6614)

PA6 GF30

AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

AKROMID®

B28 GF 33 1 GIT black (6846)

PA6 GF33

AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

Modulus

10.500MPa

Strength

190MPa

Impact

95kJ/m²

AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

AKROMID®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/m²

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

PRECITE®

Preliminary

V GF 20 2 natural (7737)

PBT-ASA- GF 20

PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/m²

PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITE®

Preliminary

E GF 30 LA black (7825)

PET GF 30

PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.

Modulus

10.500MPa

Strength

155MPa

Impact

45kJ/m²

PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.

AKROMID®

UL
Preliminary

A3 GF 30 HU black (7631)

PA66 GF30

AKROMID® A3 GF 30 HU black (7631) is a 30% glass fibre reinforced, electrical neutral heat stabilised polyamide 6.6 with high stiffness and strength, listet at UL in all colors.

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 HU black (7631) is a 30% glass fibre reinforced, electrical neutral heat stabilised polyamide 6.6 with high stiffness and strength, listet at UL in all colors.

AKROMID®

B3 ICF 15 black (5026)

PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

126272880

AKROLOY®

PA GF 50 grey (3807)PA66 + PA6I/6T GF50

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

Properties

Modulus

17.200MPa

Strength

250MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17200 MPa
16500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,7 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
360 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
105 kJ/m²
100 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
16 kJ/m²
17 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
221 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,59 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 %
0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more