Find the right compound
Select your fitting and find the right compound for your intend
PRECITEĀ®
V GF 20 2 black (7738)
PBT-ASA- GF 20
PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
6.500MPa
110MPa
50kJ/mĀ²
PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
AKROMIDĀ®
A3 GF 35 2 black (21010)
PA66 GF35
AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength
12.000MPa
185MPa
50kJ/mĀ²
AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength
PRECITEĀ®
E GF 30 LA black (7825)
PET GF 30
PRECITEĀ® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.
10.500MPa
155MPa
45kJ/mĀ²
PRECITEĀ® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.
AKROMIDĀ®
A3 GF 30 6 ECO black (8160)
PA6.6 GF30
AKROMIDĀ® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.
9.000MPa
150MPa
50kJ/mĀ²
AKROMIDĀ® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.
AKROMIDĀ®
T5 GF 35 6 black (8004)
PPA GF35
AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance
12.500MPa
230MPa
70kJ/mĀ²
AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance
AKROMIDĀ®
C28 GF 25 FRT grey (7560)
PA-Blend
AKROMIDĀ® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.
11.000MPa
135MPa
60kJ/mĀ²
AKROMIDĀ® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.
AKROMIDĀ®
A3 GF 50 1 grey (8192)
PA66 GF50
AKROMIDĀ® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
17.000MPa
260MPa
90kJ/mĀ²
AKROMIDĀ® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
T5 GF 50 8 black (6205)PPA GF50
AKROMIDĀ® T5 GF 50 8 black (6205) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures as well as moisture pic-up. The material fulfills the requirements according to ACS, WRAS and NSF 61. It is suitable for applications that are in contact with cold and hot drinking water. This material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR and is suitable for parts of kitchen and household appliances.
Regulatory
Properties
19.000MPa
270MPa
85kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Standard bending strength RP 3,5
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.