AKROMIDĀ®

Preliminary

T5 GF 35 6 black (8004)

PPA GF35

AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/mĀ²

AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

PRECITEĀ®

Preliminary

P3 8 natural (7517)

PBT

PRECITEĀ® P3 8 natural (7517) - PBT, unreinforced, food contact, medium viscosity, good dimensional stability, FDA, EU10/2011, cosmetic, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/mĀ²

PRECITEĀ® P3 8 natural (7517) - PBT, unreinforced, food contact, medium viscosity, good dimensional stability, FDA, EU10/2011, cosmetic, E&E, appliances industries.

PRECITEĀ®

Preliminary

E GF 45 ECO black (8284)

PET GF45

PRECITEĀ® E GF 45 ECO black (8284) - PET, 45% glass fiber, very high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

Modulus

16.100MPa

Strength

200MPa

Impact

65kJ/mĀ²

PRECITEĀ® E GF 45 ECO black (8284) - PET, 45% glass fiber, very high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

AKROMIDĀ®

C3 GF 35 5 XTC black (5552)

PA66+PA6 GF35

AKROMIDĀ® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.

Modulus

11.000MPa

Strength

200MPa

Impact

100kJ/mĀ²

AKROMIDĀ® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.

AKROMIDĀ®

B28 LGF 40 1 L black (6155)

PA6 + PP LGF40

AKROMIDĀ® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

Modulus

12.000MPa

Strength

200MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

AKROLOYĀ®

PA GF 60 natural (6465)

PA66+PA6I/6T GF60

AKROLOYĀ® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.000MPa

Strength

280MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

B28 GF 50 9 natural (6570)

PA6 GF50

AKROMIDĀ® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release

Modulus

17.000MPa

Strength

250MPa

Impact

115kJ/mĀ²

AKROMIDĀ® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release

125262780

AKROMIDĀ®

A3 GF 50 1 natural (1259)PA66 GF50

AKROMIDĀ® A3 GF 50 1 natural (1259) is a 50% glass fiber reinforced polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry, e.g. gearbox components. The material has a light inherent color.

Features

heat stabilised 130

Properties

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
16700 MPa
12600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
180 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
15200 MPa
13600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
380 MPa
310 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
105 kJ/mĀ²
110 kJ/mĀ²
105 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
19 kJ/mĀ²
23 kJ/mĀ²
16 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
290 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
235 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,17 10ā»ā“/K
0,88 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
160 - 175 Ā°C
130 - 150 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,57 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Water absorption

ISO 62

23Ā°C, saturated
3,7 - 4,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 ā„¦ x cm
1010 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 ā„¦
1010 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more