AKROMID®

Preliminary

B25 GF 40 L black (8452)

PA6+PP GF40

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

Modulus

11.500MPa

Strength

150MPa

Impact

60kJ/m²

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

AKROMID®

B3 GF 50 1 black (2488)

PA6 GF50

AKROMID® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

230MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

C3 GF 30 1 black (4363)

PA66+PA6 GF30

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID® C3 GF 30 1 black (4363) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROMID®

A3 GF 50 6 natural (5916)

PA66 GF50

AKROMID® A3 GF 50 6 natural (5916) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, optimized for extrusion, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

270MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 6 natural (5916) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, optimized for extrusion, technical parts in industrial engineering and automotive industry

AKROMID®

B28 GF 50 9 natural (6570)

PA6 GF50

AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release

Modulus

17.000MPa

Strength

250MPa

Impact

115kJ/m²

AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release

AKROMID®

A3 GF 30 4 6 black (13690)

PA66 GF30

AKROMID® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free

Modulus

10.000MPa

Strength

190MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 4 6 black (13690) - PA6.6, 30% glass fiber, cooling water, hydrolysis resistant, DPPD free

PRECITE®

Preliminary

E ICF 30 black (7429)

PET CF30

PRECITE® E ICF 30 black (7429) - PET, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

24.000MPa

Strength

220MPa

Impact

44kJ/m²

PRECITE® E ICF 30 black (7429) - PET, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

124252680

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)PA6 (GF15+GB15) FR(40)

AKROMID® B28 GM 15/15 1 FR black (8750) is a flame retardant PA6 reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens and red phosphorus. Due to its good flowability, it is characterised by easy processability as well as good surface properties. The product is suitable for enclosure applications in the E&E industry due to its low warpage, high stiffness and strength. This grade is excellent for laser marking.

Features

flame retardant
laser markable
surface modified
low warpage
easy flow
E&E

Regulatory

ul

Properties

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8400 MPa
5200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
105 MPa
65 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,7 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
45 kJ/m²
40 kJ/m²
40 kJ/m²
35 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
102 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
775 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,44 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,65 - 0,85 %
0,75 - 0,95 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more