AKROMID®
B3 GF 40 1 black (8353)
PA6 GF40
AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised
13.000MPa
195MPa
100kJ/m²
AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised
AKROMID®
B25 GF 40 L black (8452)
PA6+PP GF40
AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.
11.500MPa
150MPa
60kJ/m²
AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.
AKROMID®
B3 GFM 20/30 1 black (7677)
PA6 (GF20+MD30)
AKROMID® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.
14.000MPa
145MPa
45kJ/m²
AKROMID® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.
PRECITE®
P3 GK 30 natural (7643)
PBT GK30
PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
3.900MPa
50MPa
25kJ/m²
PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
AKROMID®
A3 CF 30 5 black (7488)
PA66 CF30
AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.
26.000MPa
285MPa
90kJ/m²
AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.
AKROMID®
B3 ICF 15 black (5026)
PA6 CF15
AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.
11.000MPa
140MPa
55kJ/m²
AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.
AKROMID®
C28 GF 25 FRT blue (7986)
PA-Blend
AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.
11.000MPa
145MPa
60kJ/m²
AKROMID® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.
AKROMID®
NEXT U28 ICF 40 1 black (8238)PA11 CF40
AKROMID® NEXT U28 ICF 40 1 black (8238) is a Polyamide 11 reinforced with 40% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure. The production of large-volume parts is possible with high throughputs > 1 kg/h in 3D-printing with pellets in screw extrusion additive manufacturing and Fused Granulate Fabrication (FGF).
Features
Properties
20.000MPa
190MPa
80kJ/m²
Sustainability
Biobased carbon content
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Water absorption
ISO 62
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.