AKROMID®

B3 GF 30 1 EN black (5637)

PA6 GF30

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

T5 GF 50 black (6247)

PPA GF50

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/m²

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

PRECITE®

Preliminary

E GF 40 natural (7304)

PET GF 40

PRECITE® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

15.000MPa

Strength

195MPa

Impact

64kJ/m²

PRECITE® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

E GF 20 black (7360)

PET GF 20

PRECITE® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

NA

Impact

35kJ/m²

PRECITE® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMID®

Preliminary

B3 GFM 20/30 1 black (7677)

PA6 (GF20+MD30)

AKROMID® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.

Modulus

14.000MPa

Strength

145MPa

Impact

45kJ/m²

AKROMID® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.

PRECITE®

P3 GF 20 natural (7610)

PBT GF 20

PRECITE® P3 GF 20 natural (7610) is a 20% glass fibre reinforced, lubricated poly butylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

7.200MPa

Strength

130MPa

Impact

65kJ/m²

PRECITE® P3 GF 20 natural (7610) is a 20% glass fibre reinforced, lubricated poly butylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

PRECITE®

Preliminary

P3 GF 40 black (7591)

PBT GF 40

PRECITE® P3 GF 40 black (7591) is a 40% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

13.000MPa

Strength

165MPa

Impact

70kJ/m²

PRECITE® P3 GF 40 black (7591) is a 40% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

124252680

AKROMID®

Preliminary

NEXT G3 GF 30 1 natural (8085)PA6.9 GF30

The partly bio-based AKROMID® NEXT G3 GF 30 1 natural (8085) has an increased chemical resistance and a lower moisture absorption compared to the classic PA 6 and PA 6.6. This heat stabilised and 30% glass fibre reinforced PA 6.9 is suitable for components with high demands on strength and stiffness.

Features

Bio-based
heat stabilised 130
electrically neutral
reduced moisture

Properties

Modulus

8.600MPa

Strength

160MPa

Impact

80kJ/m²

Sustainability

Biobased carbon content

56 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8600 MPa
6300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,8 %
5,3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
4,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
80 kJ/m²
80 kJ/m²
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
13 kJ/m²
14 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
195 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
219 °C

General properties

Density

ISO 1183

23°C
1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 - 1,3 %

Water absorption

ISO 62

23°C, saturated
3,0 - 3,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more