AKROMID®

UL
Preliminary

A3 GF 50 HU natural (6662)

PA66 GF50

AKROMID® A3 GF 50 HU natural (6662) is a 50% glass fibre reinforced, heat stabilised polyamide 6.6 with very high rigidity and strength, light inherent color and listet at UL in all colors

Modulus

18.000MPa

Strength

255MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 HU natural (6662) is a 50% glass fibre reinforced, heat stabilised polyamide 6.6 with very high rigidity and strength, light inherent color and listet at UL in all colors

PRECITE®

P3 GF 20 natural (7610)

PBT GF 20

PRECITE® P3 GF 20 natural (7610) is a 20% glass fibre reinforced, lubricated poly butylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

7.200MPa

Strength

130MPa

Impact

65kJ/m²

PRECITE® P3 GF 20 natural (7610) is a 20% glass fibre reinforced, lubricated poly butylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

AKROMID®

B3 GF 25 FR natural (7647)

PA6 GF25 FR(40)

AKROMID® B3 GF 25 FR natural (7647) is a 25% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0.

Modulus

9.500MPa

Strength

128MPa

Impact

73kJ/m²

AKROMID® B3 GF 25 FR natural (7647) is a 25% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0.

AKROMID®

A3 CF 30 5 black (7488)

PA66 CF30

AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Modulus

26.000MPa

Strength

285MPa

Impact

90kJ/m²

AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

AKROMID®

Preliminary

T5 GF 35 6 natural (8005)

PPA GF35

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/m²

AKROMID® T5 GF 35 6 natural (8005) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

AKROMID®

Preliminary

T5 GF 35 6 black (8004)

PPA GF35

AKROMID® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/m²

AKROMID® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

AKROMID®

UL
Preliminary

B28 GF 30 9 FR natural (8069)

PA6 GF 30 FR(40)

AKROMID® B28 GF 30 9 FR natural (8069) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

144MPa

Impact

80kJ/m²

AKROMID® B28 GF 30 9 FR natural (8069) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

123242580

AKROTEK®

Preliminary

PK-VM GF 15 natural (8680)PK GF15

AKROTEK® PK-VM GF 15 natural (8680) is a 15% glass fibre reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 15 natur (4705) in order to meet the requirements for a larger processing window during processing.

Features

hydrolysis / chemically stabilised

Properties

Modulus

4.600MPa

Strength

100MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
4600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
130 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
10 kJ/m²
10 kJ/m²
7 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
119 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,35 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,5 - 0,7 %
1,1 - 1,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more