Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
A3 GF 50 1 grey (8192)
PA66 GF50
AKROMID® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
17.000MPa
260MPa
90kJ/m²
AKROMID® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 ICF 40 AM black (8236)
PA6 CF40
AKROMID® B3 ICF 40 AM black (8236) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
27.000MPa
210MPa
45kJ/m²
AKROMID® B3 ICF 40 AM black (8236) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
AKROLOY®
PARA FGF 50 1 black (8186)
PARA FGF50
AKROLOY® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90° to the flow direction, easy flowing
19.000MPa
295MPa
75kJ/m²
AKROLOY® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90° to the flow direction, easy flowing
AKROMID®
NEXT B3 GF 30 1 L CR natural (8312)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CR natural (8312) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
A3 1 S3 natural (2847)
PA66-I
AKROMID® A3 1 S3 natural (2847) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.500MPa
65MPa
180kJ/m²
AKROMID® A3 1 S3 natural (2847) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
AKROLOY®
PA GF 60 natural (6465)
PA66+PA6I/6T GF60
AKROLOY® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
21.000MPa
280MPa
100kJ/m²
AKROLOY® PA GF 60 natural (6465) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMID®
B28 GF 50 9 natural (6570)
PA6 GF50
AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release
17.000MPa
250MPa
115kJ/m²
AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release
AKROLOY®
PARA GF 60 HU natural (8516)PARA GF60
AKROLOY® PARA GF 60 HU natural (8516) is a 60% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.
Features
Regulatory
Properties
24.000MPa
300MPa
80kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.