PRECITE®

Preliminary

K GF 30 8 natural (7882)

PBT-PET- GF 30

PRECITE® K GF 30 8 natural (7882) - PBT/PET blend, 30% glass fibre, high stiffness, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

Modulus

10.000MPa

Strength

150MPa

Impact

70kJ/m²

PRECITE® K GF 30 8 natural (7882) - PBT/PET blend, 30% glass fibre, high stiffness, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

AKROMID®

B3 ICF 15 black (5026)

PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

AKROMID®

Preliminary

B25 GF 40 L black (8452)

PA6+PP GF40

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

Modulus

11.500MPa

Strength

150MPa

Impact

60kJ/m²

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

PRECITE®

Preliminary

P3 GF 20 8 natural (8456)

PBT GF20

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

Modulus

7.200MPa

Strength

125MPa

Impact

65kJ/m²

PRECITE® P3 GF 20 natural (8456) - PBT, 20% glass fibre, food contact, very good dimensional stability, kitchen and household appliances.

AKROMID®

B3 GF 50 black (4907)

PA6 GF50

AKROMID® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

AKROMID®

B3 GF 60 4 RM-M black (5238)

PA6+X GF60

AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

Modulus

22.500MPa

Strength

225MPa

Impact

60kJ/m²

AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

AKROMID®

A3 GF 50 6 natural (5916)

PA66 GF50

AKROMID® A3 GF 50 6 natural (5916) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, optimized for extrusion, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

270MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 6 natural (5916) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, optimized for extrusion, technical parts in industrial engineering and automotive industry

123242580

AKROLOY®

Preliminary

PARA GF 35 FR grey (8200)PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR grey (8200) is a flame retardant, 35% glass-fiber reinforced Polyarylamide with highest modulus and strength. The material is based on a flame retardant system that is free of red phosphorus and halogens and is colored in grey similar to RAL 7035. Due to its very good flowability, an improved surface quality is achieved. This grade is also suitable for applications in electrical industries, which need low creep even in conditioned state.

Features

electrically neutral
flame retardant
surface modified
reduced moisture
easy flow
E&E

Properties

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
14500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
235 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 °C
800 °C
800 °C
825 °C

General properties

Density

ISO 1183

23°C
1,48 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
600 V

Dielectric strength

IEC 60243

1 mm
36 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more