HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITEĀ®

Preliminary

P3 GK 30 natural (7643)

PBT GK30

PRECITEĀ® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

Modulus

3.900MPa

Strength

50MPa

Impact

25kJ/mĀ²

PRECITEĀ® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

PRECITEĀ®

Preliminary

E GF 35 natural (7626)

PET GF 35

PRECITEĀ® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

12.600MPa

Strength

180MPa

Impact

55kJ/mĀ²

PRECITEĀ® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITEĀ®

Preliminary

V GF 20 2 black (7738)

PBT-ASA- GF 20

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/mĀ²

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITEĀ®

P3 GF 20 black (7609)

PBT GF20

PRECITEĀ® P3 GF 20 schwarz (7609) - PBT, glass fibre reinforced, higher CTI and very good dimensional stability.

Modulus

7.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 GF 20 schwarz (7609) - PBT, glass fibre reinforced, higher CTI and very good dimensional stability.

AKROMIDĀ®

A3 CF 30 5 black (7488)

PA66 CF30

AKROMIDĀ® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Modulus

26.000MPa

Strength

285MPa

Impact

90kJ/mĀ²

AKROMIDĀ® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

PRECITEĀ®

V GF 30 2 black (7724)

PBT+ASA GF30

PRECITEĀ® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

Modulus

9.500MPa

Strength

130MPa

Impact

60kJ/mĀ²

PRECITEĀ® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

PRECITEĀ®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

122232480

PRECITEĀ®

Preliminary

P3 GF 30 4 natural (8242)PBT-I GF30

PRECITEĀ®P3 GF 30 4 natur (8242) is a 30% glass fibre reinforced and hydrolysis stabilised polybutylene terephthalate (PBT). It is characterised by a high stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glycidyl methacrylate) and meets the VW-50136 standard. Furthermore, the material impresses with very good dimensional stability due to its low moisture absorption. Therefore, the material is perfectly suitable for technical precision components in applications in the automotive industry, mechanical engineering, E&E and household goods industries with increased humidity.

Features

hydrolysis / chemically stabilised
low warpage
reduced moisture
E&E
Sports & leisure

Properties

Modulus

9.000MPa

Strength

120MPa

Impact

75kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
9000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
75 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
14 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23Ā°C
1,48 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,8 - 1,0 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more