HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITE®

Preliminary

E GF 50 black (7395)

PET GF50

PRECITE® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.000MPa

Strength

210MPa

Impact

60kJ/m²

PRECITE® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

E GF 35 natural (7626)

PET GF 35

PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

12.600MPa

Strength

180MPa

Impact

55kJ/m²

PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/m²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITE®

V GF 30 2 black (7724)

PBT+ASA GF30

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

Modulus

9.500MPa

Strength

130MPa

Impact

60kJ/m²

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

AKROMID®

T5 GF 50 black (6247)

PPA GF50

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/m²

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

PRECITE®

P1 natural (7010)

PBT

PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

PRECITE®

Preliminary

E GF 50 natural (7300)

PET GF50

PRECITE® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.100MPa

Strength

220MPa

Impact

70kJ/m²

PRECITE® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

122232480

AKROMID®

UL

B3 1 FR orange (7698)PA6 FR(30)

AKROMID® B3 1 FR orange (7698) is an unreinforced, flame retardant and heat stabilised PA6, colored in orange (similar RAL 2003). Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade meets the requirements for public transportation (EN 45545-2) and is also suitable for housing, fasteners and cable connectors in the E&E markets.

Features

heat stabilised 130
flame retardant
surface modified
easy flow
E&E
public transportation

Regulatory

ul

Properties

Modulus

3.600MPa

Strength

75MPa

Impact

Na

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
75 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 10 %
> 50 %

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
4,5 kJ/m²
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,78 10⁻⁴/K
0,78 10⁻⁴/K

Thermal conductivity

DIN 52612

0,330 W/mK

Flammability

Burning rate

UL 94

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 °C
750 °C
750 °C
775 °C

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
4 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Oxygen index

ISO 4589-2

> 32 %

Protection Train

EN 45545-2

R22/23/24/26 HL3

General properties

Density

ISO 1183

23°C
1,19 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,3 - 2,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,9 - 1,1 %
1,0 - 1,2 %

Electrical Properties

Comparative tracking index

IEC 60112

UL
Test liquid A
> 600 V

Dielectric strength

IEC 60243

UL
3 mm
10 kV/mm

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
160 mm
460 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more