Select your fitting and find the right compound for your intend
PRECITE®
P3 GK 20 natural (7642)
PBT GB20
PRECITE® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
3.500MPa
50MPa
25kJ/m²
PRECITE® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
AKROMID®
A3 CF 30 5 black (7488)
PA66 CF30
AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.
26.000MPa
285MPa
90kJ/m²
AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.
AKROTEK®
PK-VM M 10 natural (7575)
PK
AKROTEK® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage
2.900MPa
58MPa
50kJ/m²
AKROTEK® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage
PRECITE®
E GF 30 LA black (7825)
PET GF 30
PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.
10.500MPa
155MPa
45kJ/m²
PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.
AKROMID®
C28 GF 25 FRT grey (7560)
PA-Blend
AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.
11.000MPa
135MPa
60kJ/m²
AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.
AKROMID®
B3 GF 40 1 HU black (8415)
PA6 GF40
AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.
12.800MPa
205MPa
100kJ/m²
AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.
AKROMID®
B3 GF 30 1 L black (4365)
PA6+PP GF30
AKROMID® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride
8.800MPa
140MPa
60kJ/m²
AKROMID® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride
AKROLOY®
AKROLOY® PA FGF 50 black (6546) is a 50% flat glass fiber reinforced, semi-aromatic polyamide blend. Due to the flat glass fiber, it is characterised by significantly improved properties 90° to the flow direction as well as low warpage. Even in conditioned state, the material impresses with very high stiffness and strength owing to its lower moisture uptake. The material is perfectly suitable for parts where dimensional stabilitiy is required. Furthermore, it can be used as an alternative for aluminium and zinc diecast alloys.
Features
Properties
17.000MPa
265MPa
100kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
IEC 60216
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.