PRECITE®

Preliminary

E GF 50 black (7395)

PET GF50

PRECITE® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.000MPa

Strength

210MPa

Impact

60kJ/m²

PRECITE® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

E GF 35 natural (7626)

PET GF 35

PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

12.600MPa

Strength

180MPa

Impact

55kJ/m²

PRECITE® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITE®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/m²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITE®

V GF 30 2 black (7724)

PBT+ASA GF30

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

Modulus

9.500MPa

Strength

130MPa

Impact

60kJ/m²

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

AKROMID®

T5 GF 50 black (6247)

PPA GF50

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/m²

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

PRECITE®

P1 natural (7010)

PBT

PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

PRECITE®

Preliminary

E GF 50 natural (7300)

PET GF50

PRECITE® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.100MPa

Strength

220MPa

Impact

70kJ/m²

PRECITE® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

122232480

AKROMID®

A3 1 L natural (4800)PA66 + PP

AKROMID® A3 1 L natural (4800) is an unreinforced PA6.6/PP-blend with reduced density compared to standard PA6.6. The material can be used where weight and cost reduction is required.

Features

heat stabilised 130
reduced density

Properties

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
55 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
30 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
80 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
7 %

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
65 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
65 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,04 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
35 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more