Description

PRECITEĀ®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

AKROMIDĀ®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

AKROMIDĀ®

Preliminary

T5 GF 35 6 black (8004)

PPA GF35

AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

Modulus

12.500MPa

Strength

230MPa

Impact

70kJ/mĀ²

AKROMIDĀ® T5 GF 35 6 black (8004) is a 35% glass fibre reinforced, inorganic high temperature stabilised polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance

PRECITEĀ®

Preliminary

P3 black (7811)

PBT

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.600MPa

Strength

60MPa

Impact

90kJ/mĀ²

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMIDĀ®

Preliminary

C28 GF 25 FRT blue (7986)

PA-Blend

AKROMIDĀ® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

145MPa

Impact

60kJ/mĀ²

AKROMIDĀ® C28 GF 25 FRT blue (7986) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 5002, Public Transportation EN 45545-2.

AKROMIDĀ®

A3 GF 50 1 grey (8192)

PA66 GF50

AKROMIDĀ® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

260MPa

Impact

90kJ/mĀ²

AKROMIDĀ® A3 GF 50 grey (8192) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

Preliminary

NEXT B3 GF 30 1 L CR black (8313)

PA6 + PP GF30

AKROMIDĀ® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/mĀ²

AKROMIDĀ® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

122232480

AKROMIDĀ®

A3 GF 25 3 black (3094)PA66 GF25

AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength

Features

nucleated

Properties

Modulus

8.500MPa

Strength

160MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8500 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,6 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
50 kJ/mĀ²
70 kJ/mĀ²
45 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
6 kJ/mĀ²
10 kJ/mĀ²

Izod notched impact strength

ISO 180/1A

23Ā°C | d.a.m.
6 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,32 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2 - 2,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,15 - 0,35 %
0,75 - 0,95 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.