PRECITEĀ®

Preliminary

E GF 50 black (7395)

PET GF50

PRECITEĀ® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.000MPa

Strength

210MPa

Impact

60kJ/mĀ²

PRECITEĀ® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITEĀ®

Preliminary

E GF 35 natural (7626)

PET GF 35

PRECITEĀ® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

12.600MPa

Strength

180MPa

Impact

55kJ/mĀ²

PRECITEĀ® E GF 35 natural (7626) - PET, 35% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITEĀ®

Preliminary

V GF 30 2 natural (7722)

PBT-ASA- GF 30

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

9.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

PRECITE V GF 30 2 natural (7722) is a 30% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITEĀ®

V GF 30 2 black (7724)

PBT+ASA GF30

PRECITEĀ® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

Modulus

9.500MPa

Strength

130MPa

Impact

60kJ/mĀ²

PRECITEĀ® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

AKROMIDĀ®

T5 GF 50 black (6247)

PPA GF50

AKROMIDĀ® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/mĀ²

AKROMIDĀ® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

PRECITEĀ®

P1 natural (7010)

PBT

PRECITEĀ® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/mĀ²

PRECITEĀ® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.

PRECITEĀ®

Preliminary

E GF 50 natural (7300)

PET GF50

PRECITEĀ® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.100MPa

Strength

220MPa

Impact

70kJ/mĀ²

PRECITEĀ® E GF 50 natural (7300) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

122232480

AKROMIDĀ®

A3 GF 30 S1 black (1365)PA66-I GF30

AKROMIDĀ® A3 GF 30 S1 black (1365) is a 30% glass fiber reinforced, impact modified Polyamide 6.6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6.6 GF 30. The material is perfectly suitable for connecting and fixing systems as well as for precision parts in the automotive industry.

Features

impact modified

Properties

Modulus

9.600MPa

Strength

180MPa

Impact

105kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9600 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
105 kJ/mĀ²
110 kJ/mĀ²
85 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
17 kJ/mĀ²
20 kJ/mĀ²
12 kJ/mĀ²
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,34 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more