PRECITE®

Preliminary

P3 GK 20 natural (7642)

PBT GB20

PRECITE® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

Modulus

3.500MPa

Strength

50MPa

Impact

25kJ/m²

PRECITE® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.

AKROMID®

A3 CF 30 5 black (7488)

PA66 CF30

AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Modulus

26.000MPa

Strength

285MPa

Impact

90kJ/m²

AKROMID® A3 CF 30 5 black (7488) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

AKROTEK®

PK-VM M 10 natural (7575)

PK

AKROTEK® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage

Modulus

2.900MPa

Strength

58MPa

Impact

50kJ/m²

AKROTEK® PK-VM M 10 natural (7575) - Polyketon, 10 % mineral reinforced Tribology, friction and wear, chemical resistance, isotropic shrinkage

PRECITE®

Preliminary

E GF 30 LA black (7825)

PET GF 30

PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.

Modulus

10.500MPa

Strength

155MPa

Impact

45kJ/m²

PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.

AKROMID®

C28 GF 25 FRT grey (7560)

PA-Blend

AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

135MPa

Impact

60kJ/m²

AKROMID® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

AKROMID®

UL

B3 GF 40 1 HU black (8415)

PA6 GF40

AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 HU black (8415) - PA 6, 40% GF, UV stabilised, high rigidity and strength, UL listed.

AKROMID®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMID® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/m²

AKROMID® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

122232480

AKROMID®

B3 natural (1024)PA6

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

Properties

Modulus

3.200MPa

Strength

83MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3200 MPa
910 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
83 MPa
43 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
4 %
20 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 30 %
> 100 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3200 MPa
1100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
25 kJ/m²
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
57 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
160 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,5 %

Water absorption

ISO 62

23°C, saturated
9 - 10 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more