AKROMIDĀ®

A3 GF 35 2 black (21010)

PA66 GF35

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

Modulus

12.000MPa

Strength

185MPa

Impact

50kJ/mĀ²

AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength

AKROMIDĀ®

B3 GF 60 4 RM-M natural (4645)

PA6 + X GF60

AKROMIDĀ® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

Modulus

21.500MPa

Strength

235MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

AKROLOYĀ®

PA FGF 50 black (6546)

PA66+PA6I/6T FGF50

AKROLOYĀ® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90Ā° to the flow direction

Modulus

17.000MPa

Strength

265MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90Ā° to the flow direction

AKROMIDĀ®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/mĀ²

AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

AKROMIDĀ®

B3 GF 30 1 black (20000)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

Modulus

9.500MPa

Strength

175MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

PRECITEĀ®

P3 GF 20 natural (7610)

PBT GF 20

PRECITEĀ® P3 GF 20 natural (7610) is a 20% glass fibre reinforced, lubricated poly butylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

7.200MPa

Strength

130MPa

Impact

65kJ/mĀ²

PRECITEĀ® P3 GF 20 natural (7610) is a 20% glass fibre reinforced, lubricated poly butylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

PRECITEĀ®

Preliminary

V GF 20 2 black (7738)

PBT-ASA- GF 20

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/mĀ²

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

121222379

AKROMIDĀ®

UL
Preliminary

A3 GF 50 HU black (6666)PA66 GF50

AKROMIDĀ® A3 GF 50 HU black (6666) is a 50 % glass fibre reinforced PA 6.6.. It is characterised by very high stiffness and strength. Furthermore, the material is electrical neutral heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry. Additionally, it is listed at UL HB in all colors.

Features

heat stabilised 130
electrically neutral
E&E
Sports & leisure
E-Mobility

Regulatory

ul

Properties

Modulus

18.000MPa

Strength

255MPa

Impact

105kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
18000 MPa
12700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
255 MPa
180 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,8 %
3,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
105 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
20 kJ/mĀ²

Thermal Properties

RTI electrical

UL 746B

UL
0,4mm Wall thickness
UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
125 Ā°C
125 Ā°C
130 Ā°C
130 Ā°C

RTI impact

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
120 Ā°C
120 Ā°C
120 Ā°C

RTI strength

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
130 Ā°C
130 Ā°C
130 Ā°C

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,14 10ā»ā“/K
1,25 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
155 Ā°C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
700 Ā°C
700 Ā°C
700 Ā°C

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
4 PLC
4 PLC
4 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,56 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1011 ā„¦ x cm

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

UL
3 mm
12 kV/mm

High voltage arc tracking rate (HVTR)

UL 746A

UL
1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

UL
5 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more