AKROMID®

B28 GF 50 natural (4842)

PA6 GF50

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/m²

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

AKROMID®

A28 GF 50 1 GIT black (5029)

PA66 GF50

AKROMID® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

Modulus

17.500MPa

Strength

270MPa

Impact

100kJ/m²

AKROMID® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

AKROMID®

B28 LGF 40 1 L black (6155)

PA6 + PP LGF40

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

Modulus

12.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

AKROMID®

T5 GF 40 black (6486)

PPA GF40

AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

14.500MPa

Strength

245MPa

Impact

80kJ/m²

AKROMID® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMID®

C3 GF 35 5 XTC black (6680)

PA66+PA6 GF35

AKROMID® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking

Modulus

11.500MPa

Strength

200MPa

Impact

105kJ/m²

AKROMID® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking

AKROMID®

B28 GF 33 1 GIT black (6846)

PA6 GF33

AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

Modulus

10.500MPa

Strength

190MPa

Impact

95kJ/m²

AKROMID® B28 GF 33 1 GIT black (6846) - 33% glass fibre reinforced, polyamide 6, heat stabilised, easy flowing, gas injection technology.

PRECITE®

Preliminary

E GF 40 natural (7304)

PET GF 40

PRECITE® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

15.000MPa

Strength

195MPa

Impact

64kJ/m²

PRECITE® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

120212280

AKROMID®

B3 GF 50 9 RM-M natural (3698)PA6 + X GF50

AKROMID® B3 GF 50 9 RM-M natural (3698) is a 50% glass fibre reinforced, process improved polyamide 6 with very high stiffness and strength, limited moisture absorption and light inherent color.

Features

reduced moisture
process improved

Properties

Modulus

16.000MPa

Strength

210MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
16000 MPa
13000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
210 MPa
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,2 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
17200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
330 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
70 kJ/m²
70 kJ/m²
60 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
20 kJ/m²
20 kJ/m²
16 kJ/m²
20 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
280 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
165 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,61 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more