AKROMID®
C3 GF 35 5 XTC black (6680)
PA66+PA6 GF35
AKROMID® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking
11.500MPa
200MPa
105kJ/m²
AKROMID® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking
AKROMID®
B28 GF 15 2 black (7060)
PA6 GF15
AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.
6.100MPa
108MPa
32kJ/m²
AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.
PRECITE®
P3 GK 20 natural (7642)
PBT GB20
PRECITE® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
3.500MPa
50MPa
25kJ/m²
PRECITE® P3 GK 20 natural (7642) is a 20% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
PRECITE®
V GF 20 2 black (7738)
PBT-ASA- GF 20
PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
6.500MPa
110MPa
50kJ/m²
PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
PRECITE®
V GF 30 2 black (7724)
PBT+ASA GF30
PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.
9.500MPa
130MPa
60kJ/m²
PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.
AKROMID®
T5 GF 30 6 black (8006)
PPA GF30
AKROMID® T5 GF 30 black (8006) is a 30% glass fibre reinforced polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance
11.800MPa
200MPa
45kJ/m²
AKROMID® T5 GF 30 black (8006) is a 30% glass fibre reinforced polyphthalamide with high rigidity and strength, as well as high temperature and chemical resistance
AKROMID®
A3 GF 40 1 LT black (5709)
PA66 GF40
AKROMID® A3 GF 40 1 LT black (5709) - 40% glass fiber reinforced PA 6.6, heat stabilised, laser transparent, for laser weldable components in the automotive and electronics industry
13.000MPa
225MPa
100kJ/m²
AKROMID® A3 GF 40 1 LT black (5709) - 40% glass fiber reinforced PA 6.6, heat stabilised, laser transparent, for laser weldable components in the automotive and electronics industry
AKROMID®
AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.
Features
Properties
11.500MPa
150MPa
60kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
UL 94
ISO 1183
ISO 1110
ISO 294-4
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.